Investigation of wear mechanisms through in situ observation during microscratching inside the scanning electron microscope

Michler, J.; Rabe, R.; Bucaille, J.-L.; Moser, B.; Schwaller, Patrick; Breguet, J.-M. (2005). Investigation of wear mechanisms through in situ observation during microscratching inside the scanning electron microscope Wear, 259(1-6), pp. 18-26. Elsevier 10.1016/j.wear.2005.02.111

[img] Text
Investigation of wear mechanisms through in situ observation during microscratching inside the scanning electron microscope.pdf - Published Version
Restricted to registered users only
Available under License Publisher holds Copyright.

Download (534kB) | Request a copy

Scratch experiments have been used in the past to investigate various contact phenomena such as abrasion mechanisms or asperity contacts. Depending on tip geometries, loading conditions and materials investigated, different crack propagation modes (radial or lateral cracks, etc.) or deformation modes (ploughing, chipping, etc.) may dominate the scratching process. The residual scratch path can yield some information about dominant deformation and fracture modes. It is, however, often not possible to uniquely correlate cracks and other phenomena with events on the recorded load–displacement curves. We have built a miniaturized microscratch device for use inside a scanning electron microscope (SEM) that allows the observation of the surface around the tip with sub-micrometer resolution during scratching. Using a conical indenter with spherical tip we demonstrate on different materials that the device is a powerful tool to observe initiation and propagation of cracks, to observe the flow of the material near the indenter (piling-up and sinking-in) and to study chip and particle formation mechanisms during microscratching. In GaAs, particles were observed to form in front and on the rear side of the tip via interaction of chevron cracks. In the case of a Fe-based bulk metallic glass, shear bands were observed to form in front of the tip leading to serrated chip formation. Discontinuities in the tip penetration during scratching of a polymer thin film were related to the onset of crack formation behind the tip and to the propagation of semi-circular cracks in front of the tip. The observed large elastic recovery of the polymer film at the rear side of the tip has to be taken into account for accurate contact area calculations.

Item Type:

Journal Article (Original Article)

Division/Institute:

School of Engineering and Computer Science > Institute for Surface Applied Laser, Phototonics and Surface Technologies ALPS
School of Engineering and Computer Science

Name:

Michler, J.;
Rabe, R.;
Bucaille, J.-L.;
Moser, B.;
Schwaller, Patrick and
Breguet, J.-M.

ISSN:

0043-1648

Publisher:

Elsevier

Language:

English

Submitter:

Patrick Schwaller

Date Deposited:

10 Dec 2019 09:18

Last Modified:

10 Dec 2019 09:18

Publisher DOI:

10.1016/j.wear.2005.02.111

ARBOR DOI:

10.24451/arbor.9296

URI:

https://arbor.bfh.ch/id/eprint/9296

Actions (login required)

View Item View Item
Provide Feedback